Mater.Phys.Mech.(MPM)
No 1, Vol. 11, 2011, pages 68-75

AGGLOMERATE SIZE IN PRECURSORS AND MECHANICAL STRENGTH OF
SOLID ELECTROLYTES BASED ON Y2O3-ZrO2 SYSTEM

V.G. Konakov, S.N. Golubev, E.N. Solovyeva, I.Yu. Archakov, N.V. Borisova, A.V. Shorokhov

Abstract

Precursor powders with the average agglomerate size of 40-1200 nm were synthesized using the reverse co-precipitation version of sol-gel method. The dependence of the mechanical strength of Y-Zr ceramics on the precursor dispersity has been studied using BET, laser PSD (particle size distribution), TEM, XRD, and DSC methods.

Keywords: Y-Zr ceramics; precursor powders; reverse precipitation sol-gel synthesis; mechanical strength of ceramics

full paper (pdf, 2528 Kb)

РАЗМЕРЫ АГЛОМЕРАТОВ В ПРЕКУРСОРАХ И МЕХАНИЧЕСКАЯ ПРОЧНОСТЬ
ТВЕРДЫХ ЭЛЕКТРОЛИТОВ НА ОСНОВЕ СИСТЕМЫ Y2O3-ZrO2

В.Г. Конаков, С.Н. Голубев, Е.Н. Соловьева, И.Ю. Арчаков, Н.В. Борисова, А.В. Шорохов

Аннотация

Методом золь-гель синтеза в варианте обратного соосаждения получены порошки-прекурсоры с различным средним размером агломератов в диапазоне 40-12000 нм. С помощью методов БЭТ, лазерной седиментографии, ТЭМ, РФА и ДСК установлена взаимосвязь между дисперсностью прекурсоров и механической прочностью Y-Zr керамик, синтезированных на основе полученных порошков-прекурсоров.

Ключевые слова: Y-Zr керамика; порошки-прекурсоры; золь-гель синтез в варианте обратного соосаждения; механическая прочность керамики

статья (pdf, 2528 Kb)