Mater.Phys.Mech.(MPM)
No 1, Vol. 14, 2012, pages 1-10

AGGLOMERATE SIZE IN PRECURSORS AND MECHANICAL
STRENGTH OF SOLID ELECTROLYTES BASED ON
Y2O3-ZrO2, Ce2O3-ZrO2 AND Ce2O3-Y2O3-ZrO2 SYSTEMS

V.G. Konakov, S.N. Golubev, E.N. Solovyeva, I.Yu. Archakov, N.V. Borisova, A.V. Shorokhov

Abstract

Precursor powders with controlled average agglomerate size in the range of 40- 12000 nm were synthesized using the reverse precipitation sol-gel. The correlation between the agglomerate size and mechanical strength of the final ceramics synthesized from these precursor powders and the content of Ce3+ and Ce4+ in the precursors was studied using BET, XRD, TEM, PSD, and DSC methods.

Keywords: nanoceramics; precursor powders; dispersity; sol-gel synthesis; solid electrolytes; mechanical strength

full paper (pdf, 2032 Kb)

РАЗМЕРЫ АГЛОМЕРАТОВ В ПРЕКУРСОРАХ И МЕХАНИЧЕСКАЯ
ПРОЧНОСТЬ ТВЕРДЫХ ЭЛЕКТРОЛИТОВ НА ОСНОВЕ СИСТЕМ
Y2O3-ZrO2, Ce2O3-ZrO2 И Ce2O3-Y2O3-ZrO2

В.Г. Конаков, С.Н. Голубев, Е.Н. Соловьева, И.Ю. Арчаков, Н.В. Борисова, А.В. Шорохов

Аннотация

Методом золь-гель синтеза в варианте обратного соосаждения получены порошки-прекурсоры с различным средним размером агломератов в диапазоне 40- 12000 нм. С помощью методов БЭТ, лазерной седиментографии, ТЭМ, РФА, ДСК и рентгеновского фотоэлектронного анализа установлена взаимосвязь между размерами агломератов в прекурсорах, механической прочностью керамик, синтезированных на основе полученных порошков-прекурсоров, и содержанием Ce3+ и Ce4+ в прекурсорах и керамиках.

Ключевые слова: нанокерамика, порошки-прекурсоры; дисперсность; золь-гель синтез; твердые электролиты; механическая прочность

full paper (pdf, 2032 Kb)