ASSESSMENT OF OPERABILITY OF THE HEAT RESISTING HP40Nb AT
OVERHEATS TO 1150 °C

S.Yu. Kondrat'ev, M.D. Fuks, G.P. Anastasiadi, A.V. Ptashnik, E.V. Sviatysheva

Abstract

Experimentally was determined long-term strength of cast heat-resistant alloy HP40Nb at the temperature of 1150 °C. It was shown that on this feature this alloy is not inferior to alloys with more nickel and tungsten, which allows rising its operational temperature range up to 1100-1150 °C. The equation, which allows calculating the value of long-term strength of the alloy HP40Nb at different values of the external stress, was found.

Keywords: heat-resistant alloy HP40Nb; strength at overheats to 1150 °C.

full paper (pdf, 1440 Kb)

ОЦЕНКА РАБОТОСПОСОБНОСТИ ЖАРОПРОЧНОГО СПЛАВА HP40Nb ПРИ
ПЕРЕГРЕВАХ ДО 1150 °С

С.Ю. Кондратьев, М.Д. Фукс, Г.П. Анастасиади, А.В. Пташник, Е.В. Святышева

Аннотация

Получены экспериментальные значения длительной прочности литого жаропрочного сплава HP40Nb при температуре 1150 °С. Установлено, что работоспособность сплава при этой температуре соответствует более легированным никелем и вольфрамом сплавам. Показана возможность повышения допустимого температурного интервала эксплуатации экономнолегированного сплава до 1100-1200 °С в установках пиролиза углеводородного сырья.

Ключевые слова: жаропрочный сплав HP40Nb; прочность при температурах до 1150 °С.

full paper (pdf, 1440 Kb)