This work is based on the use of electron backscatter diffraction (EBSD) methods to
investigate the microstructure of metastable austeniticsteel 12X18Н10T (321) after cryogenic
rolling. Cryogenic deformation was accompanied by martensitic transformations, and the
martensitic phase nucleation mainly in deformation bands. It is assumed that the proceeding of
the martensitic transformation in the most deformed parts of the microstructure should prevent
the evolution of deformation-induced boundaries in the austenite and, thus, inhibit the process
of fragmentation of this phase. Mechanical twinning was the primary (or even sole) mechanism
providing HAB formation in the austenite.
Keywords: austenitic steel, cryogenic rolling, martensite, grain boundaries, microstructure, EBSD. |
full paper (pdf, 1792 Kb)
|
Данная работа основана на использовании методики анализа картин
дифракции обратно рассеянных электронов (EBSD) для изучения микроструктуры в
метастабильной аустенитной стали 12Х18Н10Т, подвергнутой прокатке в криогенных
условиях. Криогенная деформация сопровождалась мартенситными превращениями,
причем мартенситная фаза зарождалась преимущественно в деформационных полосах.
Предположено, что протекание мартенситного превращения в наиболее
деформированных участках микроструктуры должно препятствовать эволюции границ
деформационного происхождения в аустените и, таким образом, замедлять процесс
фрагментации этой фазы. В аустенитной фазе основным механизмом формирования
большеугловых границ являлось механическое двойникование.
Ключевые слова: аустенитная сталь, криогенная прокатка, мартенсит, границы зерен, микроструктура, EBSD. |