The deformation behavior of two hard magnetic alloys 23X15KТ (Fe-23% Cr-15%
Co) and 30X23K (Fe-30% Cr-23% Co) have been studied in the temperature range
800-1050 °C and strain rates 10-1 - 10-4 s-1.
The influence of two types of structures - ultrafinegrained
and lamellar (α+γ in the 23Х15КТ alloy and γ+σ in the alloy 30Х23К) on the
superplasticity characteristics of alloys was established. During tensile straining of the 30X23K
alloy with a lamellar structure, the flow stress after 10% deformation is gradually decreased,
while in the alloy 23X15K, on the contrary, the deformation proceeds with hardening. It is
shown that the investigated alloys with an ultrafine-grained structure exhibit superplastic
behavior both under tensile straining and upsetting deformation in the temperature range of
900-950 °С and deformation rates of 10-2 - 10-4 s-1.
Keywords: superplasticity, ultrafine-grained structure, hard magnetic alloys. |
full paper (pdf, 1808 Kb)
|
Исследовано деформационное поведение двух магнитотвердых сплавов
23Х15КТ (Fe-23%Сr-15%Co) и 30Х23К (Fe-30%Cr-23%Co) в интервале температур
800-1050 °С и скоростей деформации 10-1 - 10-4 с-1. Установлено влияние двух типов
структур - ультрамелкозернистой и пластинчатой (α+γ в сплаве 23Х15КТ и γ+σ в сплаве
30Х23К) на характеристики сверхпластичности сплавов. При растяжении сплава 30Х23К
с пластинчатой структурой напряжение течения после 10% деформации плавно
снижается, а в сплаве 23Х15К, наоборот, деформация идет с упрочнением. Показано, что
исследованные сплавы с ультрамелкозернистой структурой проявляют
сверхпластическое поведение при деформации в условиях осадки и растяжения в
интервале температур 900-950 °С и скоростей деформации 10-2 - 10-4 с-1.
Ключевые слова: сверхпластичность, ультрамелкозернистая структура, магнитотвердые сплавы. |