Changes in the structure and mechanical properties of the billets from the cast nonage-hardenable
complex-alloyed 1570C alloy (Al-5Mg-0.18Mn-0.2Sc-0.08Zr, weight%) were
studied during multi-directional isothermal forging with decreasing temperature from 325 to
175°C up to cumulative strain e ≈ 24 and subsequent annealing in the temperature interval from
325 to 450°C. It is shown that the multi-directional forging with decreasing temperature can be
an effective method providing processing of billets with ultrafine grain structure with the grain
size up to 1-2 µm and a favorable combination of strength and ductility in the aluminum alloy
1570C.
Keywords: aluminum alloy, multidirectional forging, microstructural evolution, ultrafine grained structure, mechanical properties, thermal stability. |
full paper (pdf, 4240 Kb)
|
Исследованы изменения структуры и механических свойств литого
термонеупрочняемого сложнолегированного сплава 1570С (Al-5Mg-0.18Mn-0.2Sc0.08Zr,
вес.%) в процессе всесторонней изотермической ковки с понижением
температуры в интервале 325-175°С
до суммарной степени e ≈ 24 и последующего
отжига в интервале температур 325-450°С. Показано, что всесторонняя ковка с
понижением температуры является эффективным методом обработки сплавов типа
1570С, позволяющим получать объемные заготовки с однородной
ультрамелкозернистой структурой с размером зерен до 1-2 мкм и благоприятным
сочетанием параметров статической прочности и пластичности.
Ключевые слова: алюминиевый сплав, всесторонняя ковка, эволюция микроструктуры, ультрамелкозернистая структура, механические свойства, термическая стабильность. |
full paper (pdf, 4240 Kb)