Composite "phosphor-in-glass" based on high refractive index lead-silicate glass
and YAG:Ce powder has been developed and synthesized. Glass composition optimization in
the order to reduce scattering at glass/phosphor interfaces has been performed. Samples of
composite light-converting materials for white LEDs were prepared by sintering glass
powders and phosphor at 600 °С. Spectral, luminescent and structural properties of the
obtained composites have been investigated. White LEDs based on the composite glass
phosphor materials obtained have been tested. The color temperature of the probe LED was
found to be 4370 K with the luminous efficacy 58 lm/W.
Keywords: white LEDs; inorganic composite "phosphor-in-glass"; lead-silicate glass |
full paper (pdf, 1392 Kb)
|
Разработан и синтезирован люминесцирующий композит типа
"люминофор в стекле" на основе высокопреломляющей свинцово-силикатной матрицы
и мелкодисперсного порошка кристалла алюмо-иттриевого граната, активированного
церием. Произведена оптимизация состава стекла, с целью снижения потерь света при
рассеянии на границе раздела стекло-люминофор. Спеканием порошков люминофора и
стекла при температуре 600 °С получены образцы люминофоров для белых
светодиодов. Проведены рентгенофазовые и спектрально-люминесцентные
исследования полученного композита. С использованием композита "люминофор в
стекле" создан макет белого светодиода, излучающий белый свет с цветовой
температурой 4370 К, световая отдача составляет 58 лм/Вт.
Ключевые слова: белые светодиоды; неорганический композит "люминофор в стекле"; свинцово-силикатная матрица |