In this work the influence of thermal treatment and deformation processing on the microstructure, mechanical properties and electrical conductivity of ultrafine-grained (UFG) aluminum alloy Al-2Fe was considered. The UFG structure in the alloy was formed by high pressure torsion (HPT) at room temperature. As was demonstrated, HPT leads to the formation of UFG structure accompanied by the refinement of ferrum aluminide particles to nano-scale, change in their composition as well as dissolution of up to 1 wt.% Fe in aluminum. It was revealed that the optimum combination of strength and electrical conductivity in the UFG alloy can be achieved through additional ageing during annealing or subsequent straining at 200 °С.
Keywords: ultrafine-grained aluminum alloy Al-2Fe; high pressure torsion; annealing; strength; electrical conductivity. |
full paper (pdf, 1936 Kb)
|
В работе исследовано влияние термической и деформационной обработок на микроструктуру, механические свойства и электропроводность ультрамелкозернистого (УМЗ) алюминиевого сплава Al-2Fe. УМЗ структура в сплаве была сформирована интенсивной пластической деформации кручением (ИПДК) при комнатной температуре. Показано, что в результате ИПДК формирование УМЗ структуры сопровождается измельчением частиц алюминидов железа до наноразмеров, изменением их состава, а также растворением в алюминии до 1 ат.% Fe. Установлено, что достижение в УМЗ сплаве оптимального сочетания прочности и электропроводности может быть реализовано за счет использования дополнительного старения при отжиге или последующей деформации при температуре 200 °С.
Ключевые слова: ультрамелкозернистый алюминиевый сплав Al-2Fe; интенсивная пластическая деформация кручением; отжиг; прочность; электропроводность. |
full paper (pdf, 1936 Kb)