The approach for "nickel-YSZ-nanoceramics" bulk nanocomposite synthesis was developed. Compositions with the nanoceramic phase content lying in the range up to 20 wt.% YSZ were manufactured; their structure and chemical composition were studied using XRD, SEM, and EDX techniques. Experimental study of the composite mechanical properties (compressive strength) as a function of sample composition demonstrated the existence of maximal composite strength at YSZ content of 3 wt.%. Further addition of nanoceramic phase resulted in the significant decrease in material strength.
Keywords: "nickel-YSZ-nanoceramics" nanocomposite; chemical composition; microstructure; mechanical properties. |
full paper (pdf, 1520 Kb)
|
Предложена методика синтеза объемного нанокомпозита на основе мелкозернистого никеля с добавкой нанокерамической фазы на основе диоксида циркония стабилизированного оксидом иттрия. Фазовый состав и микроструктура образца изучены с использованием методов рентгеноструктурного анализа и электронной микроскопии. Данные о механических свойствах нанокомпозита позволяют констатировать, что введение в никелевую матрицу 2-3 вес.% нанокерамической фазы приводит к улучшению прочностных характеристик нанокомпозита, при дальнейшем увеличении содержания нанокерамики прочность композита существенно уменьшается.
Ключевые слова: нанокомпозит "никель-YSZ-нанокерамика"; фазовый состав; микроструктура; механические свойства. |
full paper (pdf, 1520 Kb)