The paper considers the regulation of the structural characteristics of the surface of
a new medical material - nanotitan due to the application of nanostructured titanium organic
coating brush type using the method of molecular layering ML-ALD. Established the important
role of the conditions of surface preparation of metallic substrates prior to synthesis. It
was established experimentally that by changing the temperature of the surface preparation
and the number of cycles of processing nanotitanium, you can adjust the nanorelief titanium
organic nanostructures brush type: the height of the nanostructures from 7 nm to 150 nm;
the distance between the nanostructures is from 10 to 220 nm; the size of the nanostructures
(length along the X axis) from 25 to 120 nm.
Keywords: nanotitanium; regulation of surface topography; method of molecular layering. |
full paper (pdf, 1456 Kb)
|
В работе рассмотрено регулирование структурных характеристик поверхности нового медицинского
материала - ─ нанотитана за счет нанесения наноструктурированного титанорганического покрытия
щеточного типа. Изучено регулирование нанорельефа поверхности нанотитана с помощью метода
молекулярного наслаивания (ML-ALD). Установлена важная роль условий подготовки поверхности
металлической подложки перед синтезом. Экспериментально установлено, что путем изменения
температуры подготовки поверхности и количества циклов обработки нанотитана можно регулировать
нанорельеф поверхности титана за счет титанорганических наноструктур: высота наноструктур
от 7 нм до 150 нм; расстояние между наноструктур составляет от 10 до 220 нм; Размер наноструктур (длина вдоль оси X) от 25 до 120 нм.
Ключевые слова: нанотитан; регулирование нанорельефа поверхности; метод молекулярного наслаивания. |